电工钢硅钢片_电工钢优质材料厂家直销

电工钢硅钢片In addition to the types listed above, there are also some special purpose electrical steel plates, such as 0.15 and 0.20mm thick 3％ Si cold-rolled non oriented silicon steel strips and 0.025, 0.05, and 0.1mm thick 3％ Si cold-rolled oriented silicon steel strips, used for medium and high-frequency motors, transformers, and pulse transformers； 0.7mm thick 3％ Si high-strength cold-rolled non oriented silicon steel plate for relays and power switches； High strength cold-rolled electrical steel plate for new high-speed motor rotors； Low carbon electrical steel hot-rolled thick and cold-rolled plates for magnetic shielding and high-energy accelerator electromagnets such as medical magnetic resonance tomography scanners； 4.5％ to 6.5％ Si high silicon steel plates for high-frequency motors, transformers, and magnetic shielding.Generally, motors, transformers, and other electrical components are required to have high efficiency, low power consumption, small size, and light weight. Electrical steel plates are usually guaranteed to have magnetic properties based on core loss and magnetic induction strength [1] [2]. The requirements for the performance of electrical steel plates are as follows:Low core loss (PT)Iron core loss refers to the ineffective electrical energy consumed by an iron core when magnetized in an alternating magnetic field of ≥ 50Hz, abbreviated as iron loss, also known as alternating loss, and its unit is W/kg. The ineffective electrical energy consumed due to various obstacles caused by magnetic flux changes not only loses electrical energy through the heating of the iron core, but also causes temperature rise of the motor and transformer. The iron loss (PT) of electrical steel includes three parts: hysteresis loss, eddy current loss (Pe), and anomalous loss (Pa). Electrical steel plates have low iron loss, which can save a lot of electricity, prolong the operating time of motors and transformers, and simplify cooling devices. Due to the iron loss of electrical steel plates, which accounts for 2.5％ to 4.5％ of the annual electricity generation in various countries, countries always try their best to reduce iron loss in the production of electrical steel plates, and use iron loss as the most important indicator to assess the magnetic properties of products. The iron loss value of products is used as the basis for classifying product grades. Cold rolled oriented electrical steel: Cold rolled oriented electrical steel is a high-end product in the field of electrical steel. Compared with cold rolled non oriented electrical steel, its magnetism has strong directionality； It has superior high magnetic permeability and low loss characteristics in the direction of easy magnetization rolling. The iron loss of oriented steel strip in the rolling direction is only 1/3 of that in the transverse direction, and the ratio of magnetic permeability is 6:1. Application: The main purpose of cold-rolled oriented silicon steel strip is for transformer manufacturing.Full process cold rolled non oriented silicon steel coating: The surface of the full process cold rolled silicon steel is coated with a semi transparent insulation coating, which has different codes in different standards. Taking Baosteel‘s Q/BQB 480 2014 as an example:

电工钢硅钢片B27G120表示公称厚度为0.27mm普通取向电工钢，铁损的保证值P17/50不大于1.20W/kg；B30P105表示公称厚度为0.30mm高磁感取向电工钢，铁损的保证值P17/50不大于1.05W/kg；B27R090表示公称厚度为0.27mm磁畴细化高磁感取向电工钢，铁损的保证值P17/50不大于0.90W/kg；电工钢主要分为晶粒取向电工钢和晶粒无取向电工钢两大类。取向电工钢易磁化晶粒方向沿轧制方向分布，轧制方向具有高磁感、广东中山同城低铁损及低磁致伸缩等优良特性，同时还可通过磁畴细化的技术处理，获得更低铁损的性能，广泛应用于变压器行业领域。

电工钢硅钢片：比总损耗(铁损)specific total loss (iron loss)比总损耗是指在磁极化波形保持正弦，其峰值和频率为特定值时，单位质量材料所消耗的总功率，比总损耗用符号 P(Jm/f)表示，单位为 W/kg。例：P1.0/400表示在 磁极化强度为 1.0T、广东中山频率为 400Hz 时的比总损耗。Q/BQB 481－202123.2 磁极化强度 magnetic polarization磁极化强度是指试样受交变磁化时，特定磁场强度峰值的磁极化强度峰值，其符号为 J(H)，单位为 T(特斯拉)。例：J5000表示对应于磁场强度峰值为 5000A/m 下的磁极化强度峰值。4 分类本文件的材料的等级是根据磁极化强度在1.0T、广东中山频率在400Hz下的 比总损耗值P1.0/400、广东中山材料公称厚度进行牌号分类，并按产品特性细分为普通型、广东中山高效型、广东中山高效高强度型、广东中山高磁感型和高强度型五类。