期螺强势拉涨，唐山钢坯涨20报3370元/吨，现货资源拉涨近百，从而刺激终端采买需求，整体交投氛围活跃，成交较昨日积极，考虑钢厂订货成本居高不下，商家惜售心意浓郁，预计明日建材或继续上调运行。
重量参照表
单位：Kg/m
壁 厚
外 径
3
3.5
4
4.5
5
5.5
6
32
2.146
2.460
2.762
3.052
3.329
3.594
3.847
38
2.589
2.978
3.354
3.718
4.069
4.408
4.735
42
2.885
3.323
3.749
4.162
4.562
4.951
5.327
45
3.107
3.582
4.044
4.495
4.932
5.358
5.771
50
3.477
4.014
4.538
5.049
5.549
6.036
6.511
54
3.773
4.359
4.932
5.493
6.042
6.578
7.103
57
3.995
4.618
5.228
5.826
6.412
6.985
7.546
60
4.217
4.877
5.524
6.159
6.782
7.392
7.990
63.5
4.476
5.179
5.869
6.548
7.214
7.867
8.508
68
4.809
5.567
6.313
7.047
7.768
8.477
9.174
70
4.957
5.740
6.511
7.269
8.015
8.749
9.470
73
5.179
5.999
6.807
7.602
8.385
9.156
9.914
76
5.401
6.258
7.103
7.935
8.755
9.563
10.358
89
6.363
7.380
8.385
9.378
10.358
11.326
12.281
108
7.768
9.020
10.259
11.486
12.701
13.903
15.093
133
11.178
12.725
14.261
15.783
17.294
18.792
159
13.422
15.290
17.146
18.989
20.821
22.639
219
18.601
21.209
23.805
26.388
28.959
31.517
273
23.262
26.536
29.797
33.046
36.283
39.508
325
27.750
31.665
35.568
39.458
43.337
47.202
355
38.897
43.158
47.406
51.641
377
41.339
45.871
50.390
54.897
426
46.777
51.913
57.036
62.147
450
480
530
630
单位：Kg/m
壁 厚
外 径
6.5
7
8
8.5
9
10
12
32
4.088
38
5.049
42
5.691
45
6.172
50
6.973
7.423
8.286
8.699
54
7.614
8.114
9.075
9.538
57
8.095
8.632
9.667
10.167
60
8.576
9.149
10.259
10.796
63.5
9.137
9.754
10.950
11.529
68
9.858
10.530
11.838
12.473
70
10.179
10.876
12.232
12.892
13.539
14.797
17.164
73
10.660
11.394
12.824
13.521
14.205
15.537
18.052
76
11.141
11.912
13.416
14.150
14.871
16.277
18.940
89
13.225
14.156
15.981
16.875
17.756
19.483
22.787
108
16.270
17.436
19.729
20.858
21.973
24.168
28.410
133
20.278
21.751
24.662
26.098
27.522
30.334
35.809
159
24.446
26.240
29.791
31.548
33.293
36.746
43.503
219
34.064
36.598
41.629
44.126
46.610
51.543
61.259
273
42.720
45.920
52.283
55.445
58.596
64.860
77.240
325
51.056
54.897
62.542
66.346
70.137
77.684
92.629
355
55.865
60.076
68.460
72.634
76.796
85.082
101.507
377
59.391
63.873
72.801
77.246
81.679
90.508
108.018
426
67.246
72.332
82.468
87.518
92.555
102.592
122.519
450
71.093
76.475
87.203
92.549
97.882
108.511
129.621
480
75.902
81.654
93.122
98.837
104.540
115.909
138.499
530
83.917
90.286
102.987
109.319
115.638
128.240
153.296
630
99.947
107.549
122.716
130.281
137.833
152.902
182.890
单位：Kg/m
壁 厚
外 径
3
3.5
4
4.5
5
5.5
6
32
2.146
2.460
2.762
3.052
3.329
3.594
3.847
38
2.589
2.978
3.354
3.718
4.069
4.408
4.735
42
2.885
3.323
3.749
4.162
4.562
4.951
5.327
45
3.107
3.582
4.044
4.495
4.932
5.358
5.771
50
3.477
4.014
4.538
5.049
5.549
6.036
6.511
54
3.773
4.359
4.932
5.493
6.042
6.578
7.103
57
3.995
4.618
5.228
5.826
6.412
6.985
7.546
60
4.217
4.877
5.524
6.159
6.782
7.392
7.990
63.5
4.476
5.179
5.869
6.548
7.214
7.867
8.508
68
4.809
5.567
6.313
7.047
7.768
8.477
9.174
70
4.957
5.740
6.511
7.269
8.015
8.749
9.470
73
5.179
5.999
6.807
7.602
8.385
9.156
9.914
76
5.401
6.258
7.103
7.935
8.755
9.563
10.358
89
6.363
7.380
8.385
9.378
10.358
11.326
12.281
108
7.768
9.020
10.259
11.486
12.701
13.903
15.093
133
11.178
12.725
14.261
15.783
17.294
18.792
159
13.422
15.290
17.146
18.989
20.821
22.639
219
18.601
21.209
23.805
26.388
28.959
31.517
273
23.262
26.536
29.797
33.046
36.283
39.508
325
27.750
31.665
35.568
39.458
43.337
47.202
355
38.897
43.158
47.406
51.641
377
41.339
45.871
50.390
54.897
426
46.777
51.913
57.036
62.147
450
480
530
630
单位：Kg/m
壁 厚
外 径
6.5
7
8
8.5
9
10
12
32
4.088
38
5.049
42
5.691
45
6.172
50
6.973
7.423
8.286
8.699
54
7.614
8.114
9.075
9.538
57
8.095
8.632
9.667
10.167
60
8.576
9.149
10.259
10.796
63.5
9.137
9.754
10.950
11.529
68
9.858
10.530
11.838
12.473
70
10.179
10.876
12.232
12.892
13.539
14.797
17.164
73
10.660
11.394
12.824
13.521
14.205
15.537
18.052
76
11.141
11.912
13.416
14.150
14.871
16.277
18.940
89
13.225
14.156
15.981
16.875
17.756
19.483
22.787
108
16.270
17.436
19.729
20.858
21.973
24.168
28.410
133
20.278
21.751
24.662
26.098
27.522
30.334
35.809
159
24.446
26.240
29.791
31.548
33.293
36.746
43.503
219
34.064
36.598
41.629
44.126
46.610
51.543
61.259
273
42.720
45.920
52.283
55.445
58.596
64.860
77.240
325
51.056
54.897
62.542
66.346
70.137
77.684
92.629
355
55.865
60.076
68.460
72.634
76.796
85.082
101.507
377
59.391
63.873
72.801
77.246
81.679
90.508
108.018
426
67.246
72.332
82.468
87.518
92.555
102.592
122.519
450
71.093
76.475
87.203
92.549
97.882
108.511
129.621
480
75.902
81.654
93.122
98.837
104.540
115.909
138.499
530
83.917
90.286
102.987
109.319
115.638
128.240
153.296
630
99.947
107.549
122.716
130.281
137.833
152.902
182.890
天津琪钰钢铁贸易有限公司拥有资深的技术研发团队和专业的服务团队，具备较强的科技创新能力和技术服务优势。天津琪钰钢铁贸易有限公司坚持不断创新，通过行业交流，不断提升服务品质。天津琪钰钢铁贸易有限公司始终聚焦为客户创造价值，未来，未蓝将继续在 河南钢材配件领域精耕细作，打造卓越的产品和服务，持续为客户创造价值，推动行业发展和社会进步。
热轧，顾名思义，轧件的温度高，因此变形抗力小，可以实现大的变形量。以钢板的轧制为例，一般连铸坯厚度在230mm左右，而经过粗轧和精轧，最终厚度为1~20mm。同时，由于钢板的宽厚比小，尺寸精度要求相对低，不容易出现板形问题，以控制凸度为主。对于组织有要求的，一般通过控轧控冷来实现，即控制精轧的开轧温度、终轧温度.圆管坯→加热→穿孔→打头→退火→酸洗→涂油（镀铜）→多道次冷拔（冷轧）→坯管→热处理→矫直→水压试验（探伤）→标记→入库。
连铸圆管坯低倍组织主要由3个区组成：靠外表层的等轴细晶区、像树枝状的晶体组成的柱状晶区、中心是粗大的的等轴晶区
连铸圆坯的低倍组织缺陷对管坯的加工性能、力学性能和钢管质量产生很大的影响。常见的低倍组织缺陷有：管坯皮下气泡、疏松、缩孔、皮下裂纹、中心裂纹、组织偏析等。
管坯的皮下气泡：存在连铸坯表面的附近，形态为椭圆形。一般认为钢水脱氧不足是管坯皮下气泡产生的主要原因。一般需要对保护渣、铁合金、钢包、中间包进行烘烤、注流采用保护浇注。对于要求更高的钢种，还要采用炉外精炼的方法对钢水进行脱气。存在皮下气泡的连铸圆管坯，在加热炉加热时气泡内表面会被氧化，轧后无法焊合就会形成钢管表面缺陷。
管坯皮下裂纹：存在于连铸圆管坯的柱状晶区和表面细晶区过渡附近。距离管坯表面3～10 mm。只要此裂纹不贯通到外表面，就不会被氧化，在轧制压力的作用下会焊合。一般不会产生严重的表面质量。
中间裂纹和中心裂纹：存在于连铸圆坯的柱状晶区，一般来讲中间裂纹的方向和柱状晶的方向是一致的。有研究表明，连铸管坯的中间裂纹和中心裂纹是造成无缝钢管内折的主要原因。穿孔时，管坯在轧辊和导向工具所组成的椭圆孔型中受到反复拉压应力的作用，其中间裂纹或中心裂纹得到扩张或氧化，产生钢管内折。连铸圆坯的中心裂纹或者中间裂纹扩张以后而形成的钢管内折，一般较深，常常会造成钢管废品。
管坯的疏松与缩孔：存在于管坯中心部分的等轴晶区内。管坯疏松是因为铸坯在凝固过程中超前的晶粒作用，液态金属运动基于向凝固方向冷却产生收缩受到阻碍，或者由管坯液态部分下沉的晶粒妨碍铸坯的补缩形成。当疏松达到一定程度的时候，铸坯就会出现缩孔。其分布状态在管坯中不连续。分布密度比较均匀、弥散度较高的连铸管坯中心疏松，对斜轧穿孔过程不但没有危害，反而是有利的。北京科技大学朱景清教授通过实验已经证明该点。并且，在顶头鼻部前端有一个5 mm的金属带，此金属将开裂的管坯中心与顶头分开，从而避免了内折和裂纹的缺陷。
管坯的偏析：包括组织偏析、成分偏析和结晶区域偏析等。存在穿晶的连铸管坯必须报废， 不允许投放轧管。
连铸圆管坯低倍组织主要由3个区组成：靠外表层的等轴细晶区、像树枝状的晶体组成的柱状晶区、中心是粗大的的等轴晶区
连铸圆坯的低倍组织缺陷对管坯的加工性能、力学性能和钢管质量产生很大的影响。常见的低倍组织缺陷有：管坯皮下气泡、疏松、缩孔、皮下裂纹、中心裂纹、组织偏析等。
管坯的皮下气泡：存在连铸坯表面的附近，形态为椭圆形。一般认为钢水脱氧不足是管坯皮下气泡产生的主要原因。一般需要对保护渣、铁合金、钢包、中间包进行烘烤、注流采用保护浇注。对于要求更高的钢种，还要采用炉外精炼的方法对钢水进行脱气。存在皮下气泡的连铸圆管坯，在加热炉加热时气泡内表面会被氧化，轧后无法焊合就会形成钢管表面缺陷。
管坯皮下裂纹：存在于连铸圆管坯的柱状晶区和表面细晶区过渡附近。距离管坯表面3～10 mm。只要此裂纹不贯通到外表面，就不会被氧化，在轧制压力的作用下会焊合。一般不会产生严重的表面质量。
中间裂纹和中心裂纹：存在于连铸圆坯的柱状晶区，一般来讲中间裂纹的方向和柱状晶的方向是一致的。有研究表明，连铸管坯的中间裂纹和中心裂纹是造成无缝钢管内折的主要原因。穿孔时，管坯在轧辊和导向工具所组成的椭圆孔型中受到反复拉压应力的作用，其中间裂纹或中心裂纹得到扩张或氧化，产生钢管内折。连铸圆坯的中心裂纹或者中间裂纹扩张以后而形成的钢管内折，一般较深，常常会造成钢管废品。
管坯的疏松与缩孔：存在于管坯中心部分的等轴晶区内。管坯疏松是因为铸坯在凝固过程中超前的晶粒作用，液态金属运动基于向凝固方向冷却产生收缩受到阻碍，或者由管坯液态部分下沉的晶粒妨碍铸坯的补缩形成。当疏松达到一定程度的时候，铸坯就会出现缩孔。其分布状态在管坯中不连续。分布密度比较均匀、弥散度较高的连铸管坯中心疏松，对斜轧穿孔过程不但没有危害，反而是有利的。北京科技大学朱景清教授通过实验已经证明该点。并且，在顶头鼻部前端有一个5 mm的金属带，此金属将开裂的管坯中心与顶头分开，从而避免了内折和裂纹的缺陷。
管坯的偏析：包括组织偏析、成分偏析和结晶区域偏析等。存在穿晶的连铸管坯必须报废， 不允许投放轧管。